Milky White, Porcelain White 0.38mm Laminated Glass PVB Film

• Processing Type: Multiple Extrusion
• Hardness: Soft
• Transparency: Transparent
• Surface Treatment: Stained
• Material: PVB,EVA,Sgp
• Feature: Not Self-Adhesive
• Model NO.: PVB
• Type: Glass Film
• Transport Package: Wooden Crates
• Specification: customized
• Trademark: BRG
• Origin: China
• HS Code: 7003190000
• Production Capacity: 500tons/Day

Product Description

Glass Decorative Film has high transmittance, high adhesion, high weather resistance, high crush resistance,excellent stable sunlight control system and stability of edge, which is suitable for safety laminated glass outdoor building engineer, building curtain wall, ceiling, bus glass.


Specification of  best selling architecture PVB film for safe glass

Thickness	0.38 ±0.02mm	0.76 ±0.02mm	1.14±0.02mm	1.52±0.02mm
Appearance	Primary or light yellow clear film, smooth surface without scratch or crease
Dotted Impurities and Air Bubbles	0.5-3mm not to exceed 6-8 places per roll, making marks, add an extra 1meter film per place.
Uniformity	Leteral and longitudinal evenness  shouldn't exceed 15um at a distance of 25mm;   Leteral deviation should be less than 35um, while longitudinal deviation should be less than 25 um.
Length Tolerance	+(0-2)m
Width Tolerance	+(10-20)mm
Haze (%)	<0.7(0.38 *2)
Tensile Strength(Mpa)	>=20
Elongation at break(%)	>=200

Technical Paramters of Laminated Glass EVA Film

Test item	Architectural project I	Architectural project II
Tensile strength	8.1MPA	6.4MPA
Adhesion of glass	99.7N/cm(180° peeling)	94.6N/cm(180° peeling)
Adhesion of organic polymer film	21.3N/cm(180° peeling)	15.4N/cm(180° peeling)
High transmittance	≥90.5%	≥90.9%
Haze	0.47%	0.50%
UV block rate	99%	99%
Elongation	800%	880%
Shrinkage	≤5%	≤5%
Water absorption	≤0.01%	≤0.01%
Heat-resistance In the 100°Cwater for 2 hours	No bubbles, no de-lamination	No bubbles, no de-lamination
Humidity-resistance (60°C, 95% TH 40 hours)	No bubbles or haze appeared	No bubbles or haze appeared
Anti-aging (50°C, 65% radiation 3000hours)	Light change≤3.0% No yellow change	Light change≤3.0% No yellow change
Heat & cold shock (cold 30 min, heat 80°C 30min: 50circles	No de-lamination and bubbles	No de-lamination and bubbles
Impact resistance against shot-bag	Qualified	Qualified
Ball impact peeling resistance	Qualified	Qualified
Useful life	≥15 years	≥15 years

production display

Advantage

- High tensile strength       
- Excellent transparency                  
- Outstanding adhesion
- UV protection                     
- High wind resistance                      
- Good temperature withstanding
- Water proof                       
- Humidity durable                   
- Long-term reliable                 
- Sound barrier